With outstanding physical chemical and electrical property it widely used for electrical insulation bunding to prevent corrosion and provid mechanical protection3:1 shrink ratio more suitable for application to lrregular awkward shapes.
·Very flexibie highly flame retardant(except clear)
·Operating temperature:-55℃to+135℃
·Minimum shrink temperature:70℃
·Minimum fully recovery temperature:105℃
·Standard color: Black S
·pecial color: Red Blue Yellow Green Clear (class2)
|
Property |
Test Method |
Typical Data |
|
Tensile strength |
ASTM D 2671 |
14Mpa |
|
Elongation at break |
ASTM D 2671 |
800% |
|
Tensile strength after aging(175℃/168hrs) |
ASTM D 2671 |
14Mpa |
|
Elongation after aging(175℃/168hrs) |
ASTM D 2671 |
350% |
|
Flammability |
UL 224 VW-1 |
Pass |
|
Heat shock(250℃/4hrs) |
ASTM D 2671 |
No Cracking |
|
Cold bend test(-55℃/4hrs) |
ASTM D 2671 |
No Cracking |
|
Dielectric strength |
ASTM D 150 |
20kv/mm |
|
Volume resistance |
ASTM D 876 |
1014Ω.cm |
|
Copper corrosion |
UL 224 |
Pass |
|
Water absorption |
ASTM D 570 |
0.12% |
|
Chemical resistance |
ASE-AMS-DTL-23053/5 |
Pass |
|
Longitudinal shrinkage |
UL 224 |
0±5% |
|
Eccentricity |
UL 224 |
>30% |
|
RCDRS Product Dimensions (3:1) |
|
Normal size |
As supplied(mm) |
After recovered(mm) |
Standard length(m/spool) |
|
(mm) |
(inch) |
Inside diameter(Min) |
Inside diameter(Max) |
Wall thickness(Min) |
|
RCDRS-15/0.5 |
1/16 |
1.6 |
0.5 |
0.45 |
200 |
|
RCDRS-3.0/1.0 |
1/8 |
3.2 |
1.0 |
0.55 |
200 |
|
RCDRS-4.5/1.5 |
3/16 |
4.8 |
1.5 |
0.60 |
100 |
|
RCDRS-6.0/2.0 |
1/4 |
6.4 |
2.0 |
0.65 |
100 |
|
RCDRS-9.0/3.0 |
3/8 |
9.5 |
3.0 |
0.75 |
100 |
|
RCDRS-12.0/4.0 |
1/2 |
12.7 |
4.0 |
0.80 |
50 |
|
RCDRS-18.0/6.0 |
3/4 |
19.1 |
6.0 |
0.90 |
50 |
|
RCDRS-24.0/8.0 |
1 |
15.4 |
8.0 |
1.20 |
50 |
|
RCDRS-39.0/13.0 |
11/2 |
39.0 |
13.0 |
1.25 |
50 |
|
RCDRS-50.0/17.0 |
2 |
51.0 |
17.0 |
1.30 |
50 |
|
RCDRS-60.0/20.0 |
21/2 |
65.0 |
20.0 |
1.35 |
50 |
|